PVC
(Polyvinyl Chloride) Compound
for electric cable, wire, etc.
These two grades are our standard specifications for an electric cable. We can make any kinds of custom made properties of a PVC compound up to 105��C.For more information, please contact us on our contact page.
Scroll down for the following product information
KFIC-4-75
KFIC-4-90
Other General Applications
KFIC-4-75
| KFIC-4-75 | NATURAL COLOR | QUANTITY | 45KGS | LOT NO. |
| CLASSIFICATION | UNIT | STANDARD | MEASURES | REMARKS |
| ROOM TEMP. TENSILE STRENGTH | Kg f /mm2 | 1.5 and up | 1.99 | KSM 3156 |
| ROOM TEMP.ELONGATION | % | 180 and up | 301.9 | KSM 3156 |
| TEMP. ATFER HEAT RET. OF T.S. | % | 90 and up | 98.6 | 113°C x 168HR |
| TEMP. AFTER HEATRET. OF ELONGATION | % | 80 and up | 96.4 | 113°C x 168HR |
| T/P AFTER OIL DIPRET. OF T.S. | % | 80 and up | 91.5 | ASTM NO2 OIL 100°C X96 HRS |
| T/P AFTER OIL DIPRET. OF ELONGATION | % | 75 and up | 86 | ASTM NO2 OIL 100°C X96 HRS |
| HEAT DISTORTION RATIO UNDER LOAD | % | 30 and under | 16.2 | KSM 3156 |
| BRITTLE TEMP. | -°C | -15 | -25 | KSM 3156 |
| HEAT STABILITY | ºC/ HR | 200/2 | 3.3 | KSM 3156 |
| SPECIFIC GRAVITY | Gram/cm2 | 1.416 | KSA 0602 | |
| VOLUME RESISTIVITY AT 30ºC |  cm |
 |
KSM 3156 |
KFIC-4-90
| KFIC-4-90 | NATURAL COLOR | QUANTITY | 45KGS | LOT NO. |
| CLASSIFICATION | UNIT | STANDARD | MEASURES | REMARKS |
| ROOM TEMP. TENSILE STRENGTH | Kg f /mm2 | 1.5 and up | 1.70 | KSM 3156 |
| ROOM TEMP.ELONGATION | % | 180 and up | 299 | KSM 3156 |
| TEMP. ATFER HEAT RET. OF T.S. | % | 90 and up | 101 | 113°C x 168HR |
| TEMP. AFTER HEATRET. OF ELONGATION | % | 90 and up | 99 | 113°C x 168HR |
| T/P AFTER OIL DIPRET. OF T.S. | % | 90 and up | 91.5 | ASTM NO2 OIL 100°C X96 HRS |
| T/P AFTER OIL DIPRET. OF ELONGATION | % | 90 and up | 91 | ASTM NO2 OIL 100°C X96 HRS |
| HEAT DISTORTION RATIO UNDER LOAD | % | 30 and under | 16 | KSM 3156 |
| BRITTLE TEMP. | -°C | -15 | -20 | KSM 3156 |
| HEAT STABILITY | ºC/ HR | 200/2 | 5 | KSM 3156 |
| SPECIFIC GRAVITY | Gram/cm2 | 1.43 | KSA 0602 | |
| VOLUME RESISTIVITY AT 30ºC | cm |
 |
KSM 3156 |
Other Applications
Weather Strips, Back Mirror Pad, Horn Pad, Grip, Gear Change Boots, Glass Run Channel, Door Trim
| Test Items | Grade/Unit | KFIC-1111 | KFIC-1112 | KFIC-1114 | KFIC-1116 | KFIC-1118 | KFIC-1200 |
| Specific Gravity | g/cc | 1,250 | 1,320 | 1,320 | 1,310 | 1,300 | 1,350 |
| Hardness | Shore-A | 72 | 65 | 72 | 62 | 60 | 70 |
| Tensile Strength | kg/cm2 | 130 | 92 | 83 | 94 | 91 | 130 |
| Elongation | % | 450 | 340 | 280 | 400 | 400 | 310 |
| Brittle Temperature | °C | -35 | -30 | -30 | -30 | -30 | -30 |
| Heat Loss | % | 0.5 | 0.5 | 0.5 | 0.5 | 0.5 | 0.5 |